以钢渣为主要原料制备玻璃陶瓷。

The method of manufacturing glass-ceramics using steel slag as a major raw material was described.

将废玻璃和氟云母晶体粉末混合，采用烧结法制备可加工氟闪石玻璃陶瓷。

A machinable fluoramphibole glass-ceramic was fabricated by directly mixing fluormica crystals with recycled glass powder and sintering.

制备了单向短碳化硅纤维增强玻璃陶瓷的复合材料。

The unidirectional short silicon carbide fibers reinforced-glass-ceramic matrix composite specimens were fabricated.

采用水淬法制备CBS玻璃，并使用液相参与的烧结机制制备了钙硅硼（CBS）玻璃陶瓷。

CBS glass was prepared by water-quenched method and the CBS glass-ceramic prepared by traditiona1 process-liquid phase synthesis.

金属封接玻璃陶瓷材料要求有高力学强度及与金属相匹配的热膨胀系数。

Suitable thermal expansion coefficient and high strength are prerequisite of glass-ceramics for sealing with metal.

当白榴石的掺杂量不大于50%时，掺杂白榴石可以有效地提高牙科玻璃陶瓷材料的抗折强度。

Doping leucite could effectively improve the flexural strength of dental glass-ceramics when the amount of leucite was lower than 50%.

以钢渣为主要原料制备玻璃陶瓷.

The method of manufacturing glass - ceramics using steel slag as a major raw material was described.

制备了单向短碳化硅纤维增强玻璃陶瓷的复合材料.

The unidirectional short silicon carbide fibers reinforced - glass - ceramic matrix composite specimens were fabricated.

金属封接玻璃陶瓷材料要求有高力学强度及与金属相匹配的热膨胀系数.

Suitable thermal expansion coefficient and high strength are prerequisite of glass - ceramics for sealing with metal.

具有优良下转换和近红外量子剪裁发光特性的透明玻璃陶瓷，可以对太阳光进行频谱调制。

The transparent glass ceramics with excellent down-conversion and quantum cutting luminescence performances could be used to modify the sun light frequency.